… Scale resistance up to 1150ºC, crack and wear resistant, suitable for rebuilding wornout parts. …

… prior to welding. Heavy parts and thicker plates should be preheated (150 °C), prior to welding. … Al99,0 Al.99,5 Al.99,7 E-Al., 99,5, …

… against attack of sulphourus gases at higher temperatures up to 1150 °C. When welding CEWELD 4820 AC low heat-input is required as …

… Scale resistance up to 1150ºC, crack and wear resistant, suitable for rebuilding wornout parts. …

… prior to welding. Heavy parts and thicker plates should be preheated (150°C), prior to welding  … Cast aluminium special repairs, Al99,0 …

… Weld metal provides optimum strength and oxidation resistance above 1150 °C ( 2100 °F), especially when welding on base metals of …

… be kept below 15 kJ/cm and interpass temperature between 100 and 150ºC. … Reh < 690 MPa Iso 15608: 2.2 u 3.2 ( 460 < Reh ≤ 690(700) MPa …

… anodizing. Non-heat treatable. Thicker sections should be preheated (150°C) prior to welding. … AlMgSi 0, AlSiMg (A), AlSi 1 MgMn, …

… seawater. Welding instructions: - Preheating for sections >6 mm from 150 till 300 ºC is recommended. Use the normal standard welding …

… covers a weight range of alloys. Thicker sections should be preheated (150°C) prior to welding. … Aluminium alloys: AlMg3, AlMg4, …