BASINOX 410 S
CEWELD 4009 Ti can be used for welding martensitic-ferritic steels and cast steel. Predominantly for build-ups, corrosion-resistant and wear-resistant layers. Preferred applications are sealing surfaces on gas, water and steam fittings at operating temperatures of up to 450ºC.
CEWELD 4009 Ti can be used for welding martensitic-ferritic steels and cast steel. Predominantly for build-ups, corrosion-resistant and wear-resistant layers. Preferred applications are sealing surfaces on gas, water and steam fittings at operating temperatures of up to 450ºC.
CEWELD® E 4009 Ti can be used for a working temperature of up to 450ºC. The recommended preheat temperature is 200ºC - 300°C unless the base material requires a higher preheat temperature. Use DC+ polarity and min 2 layers are required.
A tempering of 700 - 750°C is possible if required.
1.4000, 1.4001, 1.4002, 1.4003, 1.4006, 1.4008, 1.4021, 1.4024,
X6Cr13, X6CrAl13, X10Cr13, X15Cr13, X20Cr13, G-X10Cr13
AISI 410, 420
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| 725°C- 755°C 1h | 500 | 650 | 21 | 180 HB |
| As Welded | 550 | 800 | 10 | 300 HV |