CEWELD AA 309 LMo ist ein rutiler Fülldraht, der mit sehr stabilen, spritzerfreien Lichtbögen arbeitet und helle, glatte Schweißraupenoberflächen und selbstlösende Schlacke erzeugt. Dieser Draht erzeugt ein kohlenstoffarmes Schweißgut von etwa 23%Cr-13%Ni-2,3%Mo. CEWELD AA 309LMo Fülldraht kann zum erzielen einer 316L Legierung in 1 Lage verwendet werden.

For welding heat-resistant austenitic steels of the 25% Cr, 20% Ni types. AA 310 has good general oxidation resistance, especially at high temperatures, due to its high Cr content. The alloy is fully austenitic and is therefore sensitive to hot cracking. The temperature limits for use under intermittent oxidation depend on cycle frequency. In no case shall a temperature of 1000°C be exceeded. This alloy can withstand relatively severe thermic shock, and is superior to type 309L.

Very good welding characteristics and not sensitive for cracks and fissures. High tensile strength with good corrosion and acid resistance. Scale resistance up to 1150ºC, crack and wear resistant, suitable for rebuilding wornout parts. Excellent corrosion resistance against high temperature liquid acids. Much better welding characteristics than solid wire. 

CEWELD AA 316LP zeigt einen weichen Tropfenübertragung und stabilen Lichtbogen ohne Spritzerverlust, Ausgezeichnete Produktivität und Schweißbarkeit und bessere Benetzungseigenschaften im Vergleich zu Massivdrähten. Mit der Schnellerstarrende Rutilschlacke werden Röntgensichere Schweißnähte sowohl unter CO2 und Mischgas erzielt. 

Fülldraht mit Rutilschlacken für hohe Produktivität.  Hervorragend geeignet für den Einsatz auf keramischen Schweißbadsicherungen. Die Schlacke ist selbstablösend und bietet zusätzlichen Schutz, um röntgensichere Schweißnähte praktisch ohne Spritzer zu erhalten. Bessere Benetzungs- und Schweißeigenschaften bei höherer Produktivität im Vergleich zu Massivdrähten. Die 0,9 und 1,0 mm können für alle Positionen, einschließlich fallend verwendet werden und sind klassifiziert als: AWS A 5.22: E 316-LT1-4

Flux cored wire with slag support for high productivity welding in all positions. Excellent for use on ceramic backing strips. The slag is self detaching and offers extra protection to obtain X-ray proof weld seams with practically no spatters. Better wetting and welding properties with more productivity compared to solid wires

The weld deposit is scale-resistant up to approx. 800°C in normal atmosphere and oxidizing gases. The weld deposit is capable of taking a high polish. Structure: Austenite with delta ferrite. This fluxcored wire offers higher productivity, higher deposition rate and improved wetting properties due to slag support especially in positional welding. Excellent weldabillity and suitable for use with ceramic backing strips. Excellent weld metal quality and X-ray soundness. 

AA 2101 has excelent welding properties and was developed especially for the steel grade 1.4162/UNS S 32101. Due to the higher Mn and N – content of the Lean duplex base material, the slag viscosity and therefore the flow behaviour is changing and the welding bead is liquid for a longer time. The result is a very smooth seam.

Smooth drop transfer and stable arc with no spatter losses. High productivity and weldabillity, better wetting properties compared to solid wires. Ductile weld metal quality and X-ray soundness with easy slag removal and ferrite level between 30 and 50 (FN). Excellent for use in position and down hand welding. Excellent against pitting and stress corrosion.PREN above 35 weldmetal offers outstanding resistance against pitting.

CEWELD AA 2209P zeigt einen weichen Tropfenübergang und stabilen Lichtbogen ohne Spritzerverluste. Hohe Produktivität und Schweißbarkeit, bessere Benetzungseigenschaften im Vergleich zu Massivdrähten. Duktile Schweißgutqualität und Röntgentauglichkeit mit leichter Schlackenentfernung und Ferritgehalt zwischen 30 und 50 (FN). Hervorragend geeignet für Positions- und Fallnahtschweißen. Ausgezeichneter Schutz gegen Lochfraß und Spannungskorrosion. Das PREN-Schweißgut über 35 bietet eine hervorragende Beständigkeit gegen Lochfraß.