… alkalis, and some molten salts. It is especially suitable in many sulfuric, nitric, hydrochloric, and acetic acid applications. Backup …

… and suitable for applications when exposed to hydrogen sulfide or sulfur dioxide. … The nominal composition (wt.-%) of filler metal of this …

… In case of sensitive base material preheating is recommended at 300-400°C. Old Hardfacing layers should be removed, clean or grind properly …

… and a Ni-based alloy. Crushed cast carbide will guaranty a long life. Furthermore the Ni-based alloy provides an excellent corrosion …

… corrosion due to the high CrMo(N) content (Pitting index > 40). Furthermore, the weld metal alloy is saltwater-proof and offers high …

… corrosion resistance against delude hot acids. Suitable for use up to 400°C. SA 317L is best to be used in combination with FL 838 … 1.4429, …

… are used for fabrication of equipment and vessels for handling of sulfuric acid and many chloride containing media. This fluxcored wire may …

… More than 1 or 2 layers should not be deposited. Hardness reduction at 400°C app. 4%, at 650°C app. 10%. A Buffer layer with OA 4370 or OA … SMAW: Dur 64 … For fire gratings, sintering plants, augers and blast furnace bells ,gravel washing equipment, sugar mill hammer and knives, …

… than AISI 316 due to the high Mo. content. Suitable for use up to 400°C … 1.4429, 1.4434, 1.4435, 1.4436, 1.4438, 1.4439, 1.4453, …

… than AISI 316 due to the high Mo. content. Suitable for use up to 400 °C. The weld deposit is non magnetic. … Designed for joining …