12018-Mo

type 
Low hydrogen basic electrode for extreme high strenght steels
applications 
Designed for welding heat treated steels with yield strength >960 Mpa such as S960QL and TsTE960V in crane building, heavy lifting earth moving equipment etc.
Properties 

Basic electrode with excellent welding characteristics, recommended for welding fine grained similar alloyed high yield strength steel (> 960 Mpa) in case high impact values are required at sub zero temperatures. Hydrogen content (HD < 4 ml/100 g).

classification
AWS 
A 5.5: ~E 14018-G
EN ISO 
18275-A: E 89 4 ZB62 H5
DIN 
8529: EY 89 75 Mn2Ni1CrMoB H5
Suitable for 

S960QL, TSTE 960V, Xabo 90, X96, Weldox 900 Weldox 1100, Domex 960, Domex Wear 360, XABO 90, StE890V, StE960TM, weldox 900, StE 890, S890QL1, A517, X120, StE 960, S960QL1, S1100 (till 12 mm)

approvals 
CE approved
welding positions: 
Pure weld deposit

C

Mn

Si

Cr

Ni

Mo

0.07

1.65

0.50

0.90

2.60

0.85

mechanical properties

Heat treatment

RP0,2

Rm

A5

Impact energy (J) ISO-V

Hardness

(N/mm2)

(N/mm2)

(%)

-20°C

-40°C

-60°C

HRc / HV

AW

>960

>1050

>15

>47

AW: as welded
redrying temperature 
300-350ºC / 2hr
welding parameters / packing

Welding Parameters

Packing

D (mm)

Length (mm)

Current (A)

kg / can

kg / 6pack

kg / 1000

2.5

300

65-95

2.4

14.4

17.7

3.2

350

90-140

2.7

16.2

34.7

4.0

350

140-190

3.8

22.8

67.6