10018-G

type 
Ultra low hydrogen high basic offshore electrode for high strength fine grain steels.
applications 
Designed for welding steels with tensile strength >690N/mm2 in offshore, crane building, heavy transport, lifting etc.
Properties 

Mn, Ni, Cr and Mo alloyed basic electrode for welding low alloyed steels with tensile strength >690 N/mm2. Crack resistant and well suited for low-temperatures, ductility down to -60°C. Preheating, interpass temperature and post weld treatment as required for the base metal. Hydrogen content: < 3 ml / 100 g weld metal.

classification
AWS 
A 5.5: E 10018-G-H4
EN ISO 
18275-A: E 62 6 Mn2NiCrMo B 42 H5
DIN 
8529: EY 62 77 Mn2NiMo B H5
Suitable for 

S620, S550, Hardox, S620Ql1, S600MC, Naxtra 63, TStE620, Weldox 500, Hardox, Domex 460 MC, Domex 500 MC, Domex 550 MC, Domex 600 MC, Domex 650 MC, L480 - L550, X65 - X80, Hardox 400, XAR 400, Dilidur 400, 20MnCr65, 28CrMn43

approvals 
CE approved
welding positions: 
weld deposit weight %

C

Mn

Si

Cr

Ni

P

S

Mo

0.05

1.30

0.35

0.35

2.0

<0.025

<0.025

0.33

mechanical properties

Heat

RP0,2

Rm

A5

Impact energy (J) ISO-V

Hardness

treatment

(N/mm2)

(N/mm2)

(%)

-20°C

-40°C

-60°C

HRc / HV

AW

>620

>690

>17

>110

>69

>47

SR

>620

>690

>19

>32

AW: as welded / SR: stress releived (PWHT) 580°C/2hr
redrying temperature 
400°C/1 hr
welding parameters / packing

Welding Parameters

Packing

D (mm)

Length (mm)

Current (A)

kg / vacuum pack

pcs / vacuum pack

kg / master carton

2,5

350

70-90

0,8

36

8,0

3,2

350

90-125

0,7

18

7,0

4,0

350

120-160

0,8

14

8,0