AWS A5.28-1979 Mig-Tig Medium alloyed

AWS A5.28-1979

AWS

Tensile strength

Yield strength

Stretch min. %

Impact strength

Circumstances

     

classification

min. N.mm²

N/mm² ( 0.2% test )

 

Charpy V J/°C

 

     

ER 80 S-B2

550

470

19

niet vereist

*1)

     

ER 80 S-B2L

550

470

19

niet vereist

*1)

     

ER 90 S-B3

620

540

17

niet vereist

*2)

     

ER 90 S-B3L

620

540

17

niet vereist

*2)

     

ER 80 S-Ni 1

550

470

24

27 / -46

as welded 

     

ER 80 S-Ni 2

550

470

24

27 / -62

*1)

     

ER 80 S-Ni 3

550

470

24

27 / -73

*1)

     

ER 80 S-D2

550

470

17

27 / -29

as welded 

     

ER 100 S-1

690

610-700

16

68 / -51

as welded 

     

ER 100 S-2

690

610-700

16

68 / -51

as welded 

     

ER 110 S-1

760

660-740

15

68 / -51

as welded 

     

ER 120 S-2

830

730-840

14

68 / -51

as welded 

     

ER xx S-G

not required

not required

not required

not required

as welded 

     
*1) PWHT 620 +/- 15 °C.in the oven and shall be keep for one hour on tempature, cool down in the oven till 316°C and then in calm air
*2) PWHT 690 +/- 15 °C. Graden in de oven 1 uur op temeratuur gehouden, afkoelen in oven tot 316 °C. en dan in rustige lucht
                                              
                 

Achtervoegsel 

Alloy

Nominal value gew. %

           

 -B2

Cr / Mo

~ 1.3 / 0.5

           

 -B2L*

Cr / Mo

~ 1.3 / 0.5

           

 -B3

Cr / Mo

~2.5 / 1.1

           

 -B3L*

Cr / Mo

~2.5 / 1.1

           

 -Ni1

Ni

~1.0

           

 -Ni2

Ni

~2.4

           

 -Ni3

Ni

~3.4

           

 -D2 

Mn / Mo

~1.8 / 0.5

           

* C max 0.05%